1.We can supply two types MoSi2 heating elements:M1700 (heat furnace temperature 1650.C ) and M1800 (heat furnace temperature 1700.C)
2. Our standard sizes:
M1700 type (d/c): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
M1800 type (d/c): dia3/6, dia4/9, dia6/12, dia9/18, dia12/24
3. MoSi2 heating element is used to the highest temperature up to
1800C during oxidizing atmosphere. We can produce the products of
Pole, "U", "W" and "U"-right angle shapes, etc.
4. MoSi2 heating element can usually make use of furnace temperature from 1300C to 1800C. It is extensively used in the industries of metallurgy, glass, ceramic refractory,
crystal electronic device, industrial furnace manufacture, etc..
It is an essential ideal element when the products are sintering in
the high temperature.
5. Physics Characters
Volume Density Bending Strength Vickers Hardness Porosity Water
absorption Heating Elongation Rate
5.5 g/cm3 15-25 kg/cm3 (HV)570kg/mm2 7.4% 1.2% 4%
6. Chemistry Character
MoSi2 heating element is used in the high temperature under
oxidizing atmosphere. It will form the SiO2 film which can keep the
element from being melted. During the oxidizing
process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C
for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.
7.MoSi2 Heating Element's installation:
The brittleness of MoSi2 heating element is relative more under the usual temperature, it also has plasticity under the high temperature. So you had better hang and erect
vertically the "U"-shape element. If you need to erect it horizontally, please choose a support of high-temperature insulating materials. The cone-part of the element must extend
inside the furnace. At first the fixture of MoSi2 power connector can't be screwed too tightly. When temperature of the element is going up, please twist it tightly again, so the
element is not easily broken.