Detailed Product Description
|
Graphite has the good property of good resistant-corrosion,high thermal conductivity and lower friction,good self-lubrication,the smaller expansion.They can be made into the seal faces,bearings and so on.It is ideal to choose it as the frictional mating rings.
|
|
Graphite physical Property
|
|
Category
|
Model
|
Density (g/cm3)
|
Fractural Strength (MPa)
|
Compressive Strength (MPa)
|
Shaw
Hardness (HS)
|
Porosity (%)
|
Temperature
(oC)
|
|
Carbon-graphite
|
Hot molded Carbon
|
M1
|
＞1.65
|
65
|
150
|
＞70
|
＜0.2
|
180
|
|
Sintered Carbon
|
MJ
|
＞1.75
|
60
|
160
|
＞85
|
＜2.5
|
200
|
|
Impregnated Epoxy Resin(H)
|
M106H
|
1.75
|
65
|
200
|
85
|
＜1
|
250
|
|
M120H
|
1.7
|
60
|
180
|
80
|
＜1
|
250
|
|
Impregnated Furan Resin(K)
|
M106K
|
1.75
|
67
|
200
|
90
|
＜1
|
250
|
|
M120K
|
1.7
|
62
|
180
|
85
|
＜1
|
250
|
|
Impregnated Phenol Aldehyde Resin(F)
|
M106F
|
1.75
|
60
|
200
|
85
|
＜1
|
250
|
|
M120F
|
1.7
|
55
|
180
|
80
|
＜1
|
250
|
|
Antimony Carbon(D)
|
M106D
|
2.3
|
65
|
220
|
90
|
＜1.5
|
400
|
|
M120D
|
2.3
|
60
|
220
|
90
|
＜1.5
|
400
|
|
M254D
|
2.3
|
55
|
210
|
65
|
＜1.5
|
400
|
|
|